LDPE film grade is principally used in the production of blowmolding packaging film, agricultural film
and can be blended with linear lowdensity polyethylene (LLDPE) to produce modified PE.
In addition, it can be used for heat shrinkablepackaging film, laminated film, freezing film,
medical packaging, multilayer coextrusion film, heavyduty packaging film, pipe coatings, cable sheathing,
lining and high-end chemical foaming.
|
Grades
|
ECL1 |
ECL2
|
ECL3
|
ECL4
|
ECL5
|
|
MFR
|
g/10min |
2.50 |
2.40 |
0.30 |
1.5 |
2.1 |
|
Density
|
g/cm3 |
0.920 |
0.920 |
0.920 |
0.919 |
0.921 |
|
Haze
|
% |
7.5 |
7 |
14 |
24 |
10 |
|
Tensile Strength
|
MPa |
12 |
12 |
14 |
12.5 |
11 |
|
Elongation at break
|
% |
550 |
550 |
550 |
550 |
550 |
|
Grades
|
ECL6
|
ECL7
|
ECL8
|
ECL9
|
ECL10
|
|
MFR
|
g/10min |
7 |
2 |
4 |
4 |
0.31 |
|
Density
|
g/cm3 |
0.9195 |
0.9225 |
0.9225 |
0.9225 |
0.9220 |
|
Tensile Strength
|
MPa |
11 |
9 |
9 |
9 |
14 |
|
Elongation at break
|
% |
450 |
500 |
450 |
450 |
500 |
|
Grades
|
ECL11
|
ECL12
|
ECL13
|
ECL14
|
ECL15
|
|
MFR
|
g/10min |
2.8 |
4.0 |
0.3 |
2 |
2 |
|
Density
|
g/cm3 |
0.924 |
0.923 |
0.920 |
0.923 |
0.924 |
|
Haze
|
% |
10 |
10 |
15 |
9 |
9 |
|
Tensile Strength
|
MPa |
11 |
16 |
22 |
12 |
12 |
|
Elongation at break
|
% |
550 |
450 |
700 |
580 |
580 |
|
Grades
|
ECL16
|
ECL17
|
ECL18
|
ECL19
|
ECL20
|
|
MFR
|
g/10min |
2.17 |
2.17 |
4.0 |
1.9 |
0.3 |
|
Density
|
g/cm3 |
0.92 |
0.92 |
0.926 |
0.923 |
0.920 |
|
Haze
|
% |
9 |
9 |
10 |
8 |
8 |
|
Tensile Strength
|
MPa |
8 |
8 |
18 |
15 |
15 |
|
Elongation at break
|
% |
400 |
400 |
550 |
600 |
600 |